Catarina Vidal

Additive manufacturing (AM), also known as 3D printing, offers many advantages and, particularly in the medical field, it has stood out for its potential for the manufacture of patient-specific implantable devices. Thus, the unique properties of 3D-printed biocompatible polymers such as Polylactic Acid (PLA) and Polyetheretherketone (PEEK) have made these materials the focus of recent research where new post-processing and joining techniques need to be investigated. This study investigates the weldability of PLA and PEEK 3D-printed plates through stationary shoulder friction stir welding (SS-FSW) with assisted heating. An SS-FSW apparatus was developed to address the challenges of rotating shoulder FSW of thermoplastics, with assisted heating either through the shoulder or through the backing plate, thus minimizing material removal defects in the welds. Successful welds revealed that SS-FSW improves surface quality in both PLA and PEEK welds compared to rotating shoulder tools. Process parameters for PLA welds are investigated using the Taguchi method, emphasizing the importance of lower travel speeds to achieve higher joint efficiencies. In PEEK welds, the heated backing plate proved effective in increasing process heat input and reducing cooldown rates which were associated with higher crystallinity PEEK. Despite these findings, further research is needed to improve the weld strength of SS-FSW with these materials considering aspects like tool design, process stability, and 3D printing parameters. This investigation emphasizes the potential of SS-FSW in the assembly of thermoplastic materials, offering insights into the weldability of additively manufactured biocompatible polymers like PLA and PEEK.

The development of the friction stir channelling (FSC) technology has a potential to revolutionize the manufacturing industry, providing an innovative way to produce continuous sub-surface channels in monolithic components in a single step. However, the process generates heat that can lead to defects and loss of stationarity, affecting the quality of the channels produced and the process’ efficiency and control. To address these challenges, a ground-breaking study was conducted using a cooled copper backing plate to adjust the process temperatures and investigate the influence of the temperature on FSC stability. The results of the study showed that the cooled copper backing plate has a significantly higher rate of heat conduction, effectively preventing the processed component from overheating and ensuring that the process maintains its stationarity. When using the steel backing plate, only one combination of process parameters (a rotation speed of 450 rev/min and a traverse speed of 71 mm/min) yielded satisfactory results. Moreover, the use of the cooled copper backing plate allowed for a wider range of process parameters to be employed, resulting in sub-surface channels with higher quality and fewer defects. The 710/71 parameters combination resulted in a lower heat input, while the 900/45 parameters set produced channels with a more rectangular geometry. A rotation speed of 900 rev/min and a traverse speed of 45 mm/min have been shown to be the best choice. This innovative approach to FSC technology represents a major step forward in solid-state manufacturing, envisaging new possibilities for producing longer sub-surface channels with superior quality and greater efficiency. Highlights: • Conducting the FSC process at low temperature has improved its stability. • The use of a cooled copper backing plate enabled a broader range of FSC process parameters. • Longer and stabler leak-free sub-surface channels have been produced in aluminium alloys. Graphical

Structural parts’ integrity should remain as specified and designed, although it can change due to ageing and use by environmental action and accidental events. Structural parts design is carried out considering certain service conditions that can be different from operating conditions. These parts often experience dynamic solicitations that change in amplitude and frequency over time, which may cause the part’s failure. The part’s real condition can be assessed by Structural Health Monitoring systems, which grant significant social, economic, and environmental impact, as they can reduce maintenance costs and ensure the integrity of the part and its surroundings. This can be performed with an integrated monitoring system comprising sensors, on the surface or embedded, into the components. However, surface sensors are subject to damage, from collisions and/or environmental action, and embedding sensors can be very challenging and may result in a weakened part. A Self-Sensing Material (SSM) was developed based on piezoelectric particles embedded in metal parts by a solid-state processing technology. The material can act as a sensor and continuously monitor its condition. The SSM's generates an electrical voltage signal when subject to strain stimulus. Moreover, the solid-state processing technology employed promotes mechanical properties enhancement in the processed zone, not only by the grain size reduction but also due to the incorporation of the piezoelectric particles. The response to a set of dynamic loads was assessed and was found to be coherent with the solicitations applied.

A new variant of friction stir processing named upward friction stir processing (UFSP) is a promising approach to control particles’ distribution and promote a more uniform distribution over a larger processed area. This variant involves using two sheets with functional particles between them to produce metallic composites. A spacer is used to ensure the desired quantity and uniform distribution of the particles and prevent sputtering. This technique promotes an upward flow to introduce more particles with a uniform distribution in the processed volume, avoiding discrete holes or grooves. This study involved enhancing the particles’ distribution by varying process parameters. The resulting trial with the best particles’ distribution was characterized by means of light microscopy, eddy current testing, microhardness mapping, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The study revealed that UFSP can improve the particles’ distribution in the stir zone of metallic composites, especially when multi-passes are performed towards the retreating side of the plates. The process parameters that produced an improvement in particles’ distribution were six passes with an offset of 1 mm towards the retreating side, the tool rotation and processing speed of 900 rev/min, and 180 mm/min, respectively, and a spacer’s thickness of 0.5 mm. The resulting hardness and electrical conductivity profiles show that the UFSP technique can significantly affect material’s properties, including mechanical strength, particularly when processing with tool offset towards the retreating side. Furthermore, the hardness increased by about 22% in composites produced with the addition of reinforcement particles. However, for some aluminum alloys, the properties decreased under such conditions. These findings highlight the potential of UFSP for producing functionalized materials with tailored properties, while also underscoring the importance of careful parameters selection to optimize the material´s performance. Graphical Abstract

Surface metal matrix composites offer an excellent solution for applications where surface properties play a crucial role in components’ performance and durability, such as greater corrosion resistance, better wear resistance, and high formability. Solid-state processing techniques, such as friction surfacing and friction stir welding/processing, offer several advantages over conventional liquid-phase processing methods. This research investigated the feasibility of producing surface composites of aluminium-based dissimilar alloys reinforced with functional microparticles through experimental validation, determined the process parameters that resulted in a more homogeneous distribution of the particles in the surface composites, and enhanced the understanding of Upward Friction Stir Processing (UFSP) technology. The production of aluminium-based dissimilar alloys (AA 7075-T651 and AA 6082-T651) surface composites reinforced with SiC particles was studied, and it was concluded that the macrography and micrography analyses, scanning electron microscopy (SEM) analysis, microhardness measurements, and eddy currents technique reveal an extensive and homogeneous incorporation of SiC particles. In the stirred zone, a decrease of approximately 20 HV 0.5 in hardness was observed compared to the base material. This reduction is attributed to the weakening effect caused by low-temperature annealing during UFSP, which reduces the strengthening effect of the T651 heat treatment. Additionally, the presence of particles did not affect the surface composite hardness in the stirred zone. Furthermore, despite the presence of significant internal defects, SEM analyses revealed evidence of the lower alloy merging with the upper zone, indicating that the lower plate had a role beyond being merely sacrificial. Therefore, the production of bimetallic composites through UFSP may offer advantages over composites produced from a monometallic matrix. The results of the eddy currents testing and microhardness measurements support this finding and are consistent with the SEM/EDS analyses.

Sensing Technology (ST) plays a key role in Structural Health-Monitoring (SHM) systems. ST focuses on developing sensors, sensory systems, or smart materials that monitor a wide variety of materials’ properties aiming to create smart structures and smart materials, using Embedded Sensors (ESs), and enabling continuous and permanent measurements of their structural integrity. The integration of ESs is limited to the processing technology used to embed the sensor due to its high-temperature sensitivity and the possibility of damage during its insertion into the structure. In addition, the technological process selection is dependent on the base material’s composition, which comprises either metallic or composite parts. The selection of smart sensors or the technology underlying them is fundamental to the monitoring mode. This paper presents a critical review of the fundaments and applications of sensing technologies for SHM systems employing ESs, focusing on their actual developments and innovation, as well as analysing the challenges that these technologies present, in order to build a path that allows for a connected world through distributed measurement systems.

Friction Stir Welding is a process that has led to increasing usage of aluminum and its alloys in different industries, since it is an autogenous and a solid-state welding process. The work developed in this paper was focused on the analysis of the mechanical behavior of AA7075-T651 friction stir butt welded joints, of 4 mm of thickness, under different loading and temperature conditions. A selection process was applied to assure the appropriate welding parameters. The welds from which the investigated specimens were manufactured from were submitted to nondestructive testing to assess the presence of welding defects. Fatigue tests were carried out, under a constant amplitude loading regime, at stress ratios of 0.05 and 0.5 and at temperatures of 23 °C and 150 °C. The results obtained by the fatigue tests point to a higher fatigue life of the specimens when the highest stress ratio, R = 0.5, was used (for the maximum stress applied), for both loading temperatures. For the stress range, the contrary was found to be true. Room temperature was also found to result in a significantly better fatigue performance. A Scanning Electron Microscope was used to characterize the fatigue fracture surfaces.