Harumi Tsutsumi
Current Organizations / Institutes
The organizations/institutes from the scholar's latest article
Research Subjects
Harumi Tsutsumi has a total of 16 co-authors. Here are the top co-authors by number of shared publications:
Hideki Katayama
Research Center for Structural Materials, National Institute for Materials Science (NIMS)
1 shared publication- Hideki Katayama
Research Center for Structural Materials, National Institute for Materials Science
1 shared publication Kunio Ishikawa
Department of Biomaterials, Faculty of Dental Science, Kyushu University
1 shared publication- Kunio Ishikawa
Department of Biomaterials, Faculty of Dental Science, Kyushu University, Fukuoka, Japan
1 shared publication Maki Ashida
Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University (TMDU)
1 shared publication- Maki Ashida
Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University (TMDU), 2-3-10 Kanda-Surugadai, Chiyoda, Tokyo 101-0062, Japan
1 shared publication
Latest Publications
- Open Access
Investigation of the Long-Term Antibacterial Properties of Titanium by Two-Step Micro-Arc Oxidation Treatment
Recently, biofilm formation caused by bacterial adhesion and colonization has been recognized as the major cause of failure in orthopedic and dental implant surgeries. In this study, a customized micro-arc oxidation (MAO) treatment technique was developed to obtain desirable antibacterial properties on Ti surfaces. The two-step MAO treatment was applied in the fabrication of specimens with Ag and with/without Zn in their surface oxide layer. In order to simulate practical usage, surface analyses and immersion tests were performed to evaluate the incorporation of Ag and Zn into the resulting oxide layer and ion release behavior, respectively. Additionally, the antibacterial properties of the specimens after long-term immersion in physiological saline were evaluated using Gram-negative facultative anaerobic bacteria. The MAO-treated specimens containing Ag and Zn exhibited excellent antibacterial properties against Escherichia coli, which were sustained even after 6 months of immersion in physiological saline to simulate practical usage. Moreover, the Ag ions released from the surface oxide indicate the antibacterial properties of the specimen in the early stage, while the release of the corrosion products of Zn demonstrates its antibacterial properties in the later stage.
Open AccessInvestigation of the Long-Term Antibacterial Properties of Titanium by Two-Step Micro-Arc Oxidation Treatment
Recently, biofilm formation caused by bacterial adhesion and colonization has been recognized as the major cause of failure in orthopedic and dental implant surgeries. In this study, a customized micro-arc oxidation (MAO) treatment technique was developed to obtain desirable antibacterial properties on Ti surfaces. The two-step MAO treatment was applied in the fabrication of specimens with Ag and with/without Zn in their surface oxide layer. In order to simulate practical usage, surface analyses and immersion tests were performed to evaluate the incorporation of Ag and Zn into the resulting oxide layer and ion release behavior, respectively. Additionally, the antibacterial properties of the specimens after long-term immersion in physiological saline were evaluated using Gram-negative facultative anaerobic bacteria. The MAO-treated specimens containing Ag and Zn exhibited excellent antibacterial properties against Escherichia coli, which were sustained even after 6 months of immersion in physiological saline to simulate practical usage. Moreover, the Ag ions released from the surface oxide indicate the antibacterial properties of the specimen in the early stage, while the release of the corrosion products of Zn demonstrates its antibacterial properties in the later stage.
- 25 May 2021
- Published by Japanese Society for Dental Materials and Devices in Dental Materials Journal
- Vol. 40 (3) , 592-598
Enhancement of antibacterial property of titanium by two-step micro arc oxidation treatment
A customized micro arc oxidation (MAO) treatment technique was developed to obtain desirable antibacterial properties on titanium surfaces. The two-step MAO treatment was applied to fabricate a specimen containing both Ag and Zn in its surface oxide layer. Surface analyses and metal-ion release tests were performed to evaluate the presence of Ag and Zn and the ion release behavior for simulating practical usage, respectively. Additionally, the antibacterial properties of the specimens were also evaluated using gram-negative facultative anaerobic bacteria. The MAO-treated specimens containing both Ag and Zn showed excellent antibacterial properties against Escherichia coli, and the properties were sustained even after 28 days of immersion in physiological saline to simulate the living environment.
- 25 May 2021
- Published by Japanese Society for Dental Materials and Devices in Dental Materials Journal
- Vol. 40 (3) , 592-598
Enhancement of antibacterial property of titanium by two-step micro arc oxidation treatment
A customized micro arc oxidation (MAO) treatment technique was developed to obtain desirable antibacterial properties on titanium surfaces. The two-step MAO treatment was applied to fabricate a specimen containing both Ag and Zn in its surface oxide layer. Surface analyses and metal-ion release tests were performed to evaluate the presence of Ag and Zn and the ion release behavior for simulating practical usage, respectively. Additionally, the antibacterial properties of the specimens were also evaluated using gram-negative facultative anaerobic bacteria. The MAO-treated specimens containing both Ag and Zn showed excellent antibacterial properties against Escherichia coli, and the properties were sustained even after 28 days of immersion in physiological saline to simulate the living environment.