Laser welding of austenitic ferrofluid container for the KRAKsat satellite

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The production of a ferrofluid container, intended for use in the KRAKsat (CubeSat type) satellite in space conditions, is presented. Mechanized laser beam welding for AISI 316L stainless steel test joint and container prototype was developed and tested. The welded test joints were examined by non-destructive visual, penetration and radiographic testing and destructive testing by macro- and microscopic examination, static tensile test, static bending test, and hardness measurements. The welded container prototype was examined by leak test, temperature-vacuum test and vibration test. Test joints’ evaluation showed a proper selection of welding parameters and expected quality of joints. Austenitic microstructure with small δ-ferrite content in base materials, heat-affected zones, and welds guarantees sufficient mechanical properties for this part geometry. The tensile strength range of test joints was 687–729 MPa, hardness range was 140–200 HV3, and the bending angle was 180°. Welding of the prototype container and testing of tightness, resistance to temperature changes, and vibration were successful. Compliance with flywheel design and manufacturing requirements will enable the launch of a research satellite into orbit with such a wheel.
Funding Information
  • Ministerstwo Nauki i Szkolnictwa Wyższego (16.16.110.663)

This publication has 42 references indexed in Scilit: