A hundred times faster: Novel, rapid sol‐gel synthesis of bio‐glass nanopowders (Si‐Na‐Ca‐P system, Ca:P = 1.67) without aging

Authors:
Publisher website
Google Scholar
Abstract
Synthesis of sol‐gel glass with incorporation of Na 2 O is extremely difficult, as such glasses have a great tendency to crystallize. Slow drying and aging over several days or weeks is usually required in sol‐gel preparation procedures. This work reports a fast, novel route for the synthesis of bioglass powders in a considerably shortened period of 1 h. A comparative study of sol‐gel derived glasses made by this novel route using rotary evaporator drying, and a conventional route using oven drying and aging, revealed that the two methods produce stabilized (devitrified) bio‐glasses with virtually identical behavior and properties. Indeed, the rapidly dried powder exhibited slightly enhanced properties that should result in improved bioactivity. Fourier‐transform infrared spectroscopy was used to understand the structures of the synthesized powders, and MAS ‐ NMR was used to look at the degree of polymerization. This innovative, rapid route was successfully demonstrated to produce glass and devitrified glass nanopowders more than one hundred times quicker than the quickest reported standard drying methods.
Funding Information
  • Fundação para a Ciência e a Tecnologia (SFRH/BPD/97115/2013, UID /CTM /50011/2013)
  • Federación Española de Enfermedades Raras

This publication has 27 references indexed in Scilit: