An Enhanced Vacuum-Assisted Resin Transfer Molding Process and Its Pressure Effect on Resin Infusion Behavior and Composite Material Performance

Authors:
Open Access
Publisher website
Google Scholar
Abstract
In this paper, an enhanced VARTM process is proposed and its pressure effect on resin infusion behavior and composite material performance is studied to reveal the control mechanism of the fiber volume fraction and void content. The molding is vacuumized during the resin injection stage while it is pressurized during the mold filling and curing stages via a VARTM pressure control system designed in this paper. Theoretical calculations and simulation methods are used to reveal the resin’s in-plane, transverse, and three-dimensional flow patterns in multi-layer media. For typical thin-walled components, the infiltration behavior of resin in isotropic porous media is studied, elucidating the control mechanisms of fiber volume fraction and void content. The experiments demonstrate that the enhanced VARTM process significantly improves mold filling efficiency and composite’s performance. Compared to the regular VARTM process, the panel thickness is reduced by 4% from 1.7 mm, the average tensile strength is increased by 7.3% to 760 MPa, the average flexural strength remains at approximately 720 MPa, porosity is decreased from 1.5% to below 1%, and the fiber volume fraction is increased from 55% to 62%.
Funding Information
  • Special Funds for Hunan Science and Technology Innovation Program (2021GK1020, 2022GK1070, 2022JJ50011)
  • Construction of Innovative Provinces in Hunan (2021GK1020, 2022GK1070, 2022JJ50011)
  • Natural Science Foun-dation, Hunan Province (2021GK1020, 2022GK1070, 2022JJ50011)

This publication has 31 references indexed in Scilit: