Investigation into stress recovery behavior of shape memory polyurethane fiber

Authors:
Publisher website
Google Scholar
Abstract
In this work, the stress recovery behavior of shape memory polyurethane (SMPU) fiber was investigated. The as‐spun SMPU fibers were subjected to various programing‐recovery conditions. It was observed that recovering at 100 °C generated higher recovery stress than recovering at 150 °C. It was also found that, while hot‐drawn programed fiber has higher recovery stress than cold‐drawn programed fiber if recovered at 100 °C, cold‐drawn programed fiber has higher stabilized recovery stress than hot‐drawn programed counterpart when recovered at 150 °C. A morphological model was proposed based on the results from differential scanning calorimetry, Fourier transform infrared spectrometry, and X‐ray diffraction to understand the physics behind the different stress recovery behaviors. It is found that SMPU experiences different phase transitions and phase separations under different programing and stress recovery conditions. It is concluded that the two sequential phase separations taking place at 100 and 150 °C are primarily responsible for the differences in the stress recovery behavior. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014, 52, 1429–1440
Funding Information
  • National Science Foundation (1333997)

This publication has 66 references indexed in Scilit: