Room temperature processable heat‐resistant epoxy‐oxazolidone‐based syntactic foams

Authors:
Publisher website
Google Scholar
Abstract
Syntactic foams based on oxazolidone‐modified epoxy resin using glass microballoons as reinforcing filler with varying densities were processed. The influence of various grades of microballoons and their concentration on the mechanical, thermal, thermomechanical, and flammability characteristics were investigated. The effect of temperature on the compressive strength with density was monitored in detail. By incorporating the microballoons, Tg of the syntactic foam increased from 90 °C to 115 °C. Thermal conductivity was found to decrease from (0.064 to 0.056 W/(m·K)) in conjunction with decreasing resin to filler ratio. In the case of composites filled with K25 alone, the creation of large voids due to less effective packing between the microballoons led to lower thermal conductivity. The specific heat of the different composites was in the range of 0.32 to 0.44 cal/g/°C, and the coefficient of thermal expansion was in the range of 13.2 to 17.4 × 10−6/°C with limiting oxygen index of 28% to 33%.

This publication has 38 references indexed in Scilit: