Effect of Energy Alignment, Electron Mobility, and Film Morphology of Perylene Diimide Based Polymers as Electron Transport Layer on the Performance of Perovskite Solar Cells

Authors:
Publisher website
Google Scholar
Abstract
For organic–inorganic perovskite solar cells (PerSCs), the electron transport layer (ETL) plays a crucial role in efficient electron extraction and transport for high performance PerSCs. Fullerene and its derivatives are commonly used as ETL for p–i–n structured PerSCs. However, these spherical small molecules are easy to aggregate with high annealing temperature and thus induce morphology stability problems. N-type conjugated polymers are promising candidates to overcome these problems due to the tunable energy levels, controllable aggregation behaviors, and good film formation abilities. Herein, a series of perylene diimide (PDI) based polymers (PX-PDIs), which contain different copolymeried units (X), including vinylene (V), thiophene (T), selenophene (Se), dibenzosilole (DBS), and cyclopentadithiophene (CPDT), are introduced as ETL for p–i–n structured PerSCs. The effect of energy alignment, electron mobility, and film morphology of these ETLs on the photovoltaic performance of the PerSCs are fully investigated. Among the PX-PDIs, PV-PDI demonstrates the deeper LUMO energy level, the highly delocalized LUMO electron density, and a better planar structure, making it the best electron transport material for PerSCs. The planar heterojunction PerSC with PV-PDI as ETL achieves a power conversion efficiency (PCE) of 10.14%, among the best values for non-fullerene based PerSCs.
Funding Information
  • Ministry of Education of the People's Republic of China (2015ZZD06, 2016YQ06, JB2015RCJ02)
  • Ministry of Science and Technology of the People's Republic of China (2015CB932201)
  • Natural Science Foundation of Beijing Municipality (2162045)
  • National Natural Science Foundation of China (51573042)
  • Chinese Academy of Sciences (QYZDBSSW-SLH033)
  • Science and Technology Support Program of Jiangsu Province (BE2014147-4)

This publication has 42 references indexed in Scilit: