The characteristics and formation mechanism of the dark rim in alkali-activated slag
Authors:
- Zijian JiaZJZijian Jia
- Chun ChenCCChun Chen
- Hongyu ZhouHZHongyu Zhou
- Yamei ZhangYZYamei Zhang
- 1 September 2020
- journal article
- research article
- Published by Elsevier in Cement and Concrete Composites
- Vol. 112
Abstract
No abstract availableKeywords
Funding Information
- National Natural Science Foundation of China (51972057, 51778132)
This publication has 32 references indexed in Scilit:
- Characterization of alkali activated slag paste after exposure to high temperaturesConstruction and Building Materials, 2013
- Assessment of CO2 reduction of alkali-activated concreteJournal of Cleaner Production, 2013
- Properties and durability of alkali-activated slag pastes immersed in sea waterCeramics International, 2012
- Advances in alternative cementitious bindersCement and Concrete Research, 2011
- Freeze–thaw cycle test and damage mechanics models of alkali-activated slag concreteConstruction and Building Materials, 2011
- Costs and carbon emissions for geopolymer pastes in comparison to ordinary portland cementJournal of Cleaner Production, 2011
- The role of inorganic polymer technology in the development of ‘green concrete’Cement and Concrete Research, 2007
- Resistance of alkali-activated slag concrete to acid attackCement and Concrete Research, 2003
- Alkali-activated cements Opportunities and challengesCement and Concrete Research, 1999
- The characterization of hardened alkali-activated blast-furnace slag pastes and the nature of the calcium silicate hydrate (C-S-H) phaseCement and Concrete Research, 1994