Hybrid PEDOT Conductive Polymer-Powdered Metal Sulfide Photocathodes for Photoelectrochemical Green H 2 Production

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Hybrid photocathodes combining metal sulfide powders with poly-3,4-ethylenedioxythiophene (PEDOT) as an effective hole transporting polymer were prepared through a facile drop-casting method and electrochemically oxidative polymerization of 3,4-ethylenedioxythiophene (EDOT). The PEDOT modification remarkably enhanced a photocurrent density of a powder-based (CuGa)0.5ZnS2 photocathode (bandgap (BG): 2.3 eV) for hydrogen evolution under visible light irradiation at 0 V vs RHE, 60-times higher compared with an unmodified photocathode. The improvement was advantageously effective when using small metal sulfide particles prepared by a flux method compared to large particles synthesized by a solid-state reaction due to improved necking and interfacial contact facilitated by PEDOT in the fine physical structure. The optimized PEDOT/(CuGa)0.5ZnS2-composited photocathode (PEDOT-(CuGa)0.5ZnS2) achieved an incident photon-to-current conversion efficiency (IPCE) of 30% at 420 nm and 0 V vs RHE for the H2 evolution. PEDOT modification was also effective for Cu2ZnSnS4 (BG: 1.4 eV) and Cu3VS4 (BG: 1.5 eV) black metal sulfide photocathodes. Furthermore, solar water splitting proceeded in a two-electrode photoelectrochemical cell consisting of a PEDOT-(CuGa)0.5ZnS2 photocathode and a BiVO4-based photoanode, even without applying an external bias. The photoelectrochemical cell gave 0.08% for nonbias and 0.21% for 0.4 V of an external bias of a solar-to-hydrogen energy conversion efficiency (STH), even though both photoelectrodes were fabricated without any vacuum process and using just two ingredients. Our findings will offer a viable strategy for developing photocathodes that unite simplicity and high performance by using powder materials for the scalable application of photoelectrochemical green H2 production.
Funding Information
  • Japan Society for the Promotion of Science (23H00248)
  • Support for Pioneering Research Initiated by the Next Generation (JPMJSP2151)
  • Tokyo University of Science

This publication has 51 references indexed in Scilit: