In vitro characterization of peptide-modified p(AAm-co-EG/AAc) IPN-coated titanium implants

Authors:
Publisher website
Google Scholar
Abstract
Interpenetrating polymer networks (IPNs) of poly(acrylamide‐co‐ethylene glycol/acrylic acid) [p(AAm‐co‐EG/AAc)] functionalized with an ‐Arg‐Gly‐Asp‐ containing peptide derived from rat bone sialoprotein [bsp‐RGD(15)] were grafted to titanium implants in an effort to modulate osteoblast behavior in vitro. Surface characterization data were consistent with the presence of an IPN, and ligand density measurements established that the range of peptide density on the modified implants spanned three orders of magnitude (0.01–20 pmol/cm2). In vitro biological characterization of the modified implants employing the primary rat calvarial osteoblast (RCO) model resulted in the identification of a critical ligand density (0.01 < Γcrit < 0.1 pmol/cm2) for maximal support of the osteoblast phenotype. After 14 and 21 days, mineralization was greater on the 0.1 and 10 pmol/cm2 bsp‐RGD(15) modified implants compared to the base titanium and other control surfaces. The observed effects were attributed to specific interactions with bsp‐RGD(15) and support the concept that peptide‐modified implants can enhance the kinetics of differentiation of the cells they contact. These results suggest that in vivo biological performance evaluation of these biomimetic implant surfaces is merited. © 2006 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 24:1366–1376, 2006

This publication has 27 references indexed in Scilit: