The morphological, mechanical, rheological, and thermal properties of PLA/PBAT blown films with chain extender

Authors:
Publisher website
Google Scholar
Abstract
Biodegradable poly(lactic acid) (PLA)/poly(butylene adipate‐co‐terephthalate) (PBAT) blends and films were prepared using melt blending and blowing films technique in the presence of chain extender‐Joncryl ADR 4370F. The ADR contains epoxy functional groups and used as a compatibilizer. The morphological, mechanical, rheological, thermal, and crystalline properties of the PLA/PBAT/ADR blown films were studied. Scanning electron microscopy micrographs of the films revealed more ductile deformation with increasing PBAT content. The addition of PBAT enhanced the toughness of the PLA film. Tensile tests indicated that the elongation at break increased from 20.5% to 334.6% in the machine direction and from 7.1% to 715.9% in the transverse direction. The Young modulus increased from 2690.5 to 395.6 MPa in the machine direction and from 2623.5 to 154.0 MPa in the transverse direction. The sealing strength of 40/60/0.15 PLA/PBAT/ADR film was the highest among all the samples up to 9.4 N 15 mm−1. These findings gave important implications for designing and manufacturing polymer packaging materials.
Funding Information
  • National Key Research and Development Program of China (No. 2016YFC0501402)
  • Science & Technology Bureau of Jilin Province of China (No. 20170204012SF, No. 20160307001GX)
  • Chinese Science Academy (Changchun Branch) (2017SYHZ0018, No. 2017SYHZ0016)
  • Science & Technology Bureau of Jilin City of China (No. 20163206)
  • Science & Technology Bureau of Changchun City of China (No. 16SS03)

This publication has 47 references indexed in Scilit: