Evolution of Creep Damage and its Effect on the Carburization Behavior of Centrifugally Cast 25Cr35NiNb Alloy

This publication has 29 references indexed in Scilit:

• Microstructure evolution and creep behavior of nitrogen-bearing austenitic Fe–Cr–Ni heat-resistant alloys with various carbon contents
  Journal of Materials Research and Technology, 2023
• Effect of microstructural evolution in thermal exposure on mechanical properties of HP40Nb alloy
  International Journal of Pressure Vessels and Piping, 2021
• Evolution of Microstructure and Creep Behavior in an Fe-Ni-Cr-Nb-C Alloy during Service in Hydrocarbon Cracker Tubes
  Journal of Materials Engineering and Performance, 2019
• Failure analyses of centrifugal casting ethylene pyrolysis furnace tubes from microporosity defects
  Engineering Failure Analysis, 2019
• Material degradation and embrittlement evaluation of ethylene cracking furnace tubes after long term service
  Engineering Failure Analysis, 2019
• Fragmented structure of niobium carbide particles in as-cast modified HP alloys
  Acta Materialia, 2017
• Experimental observation and crystallographic description of M7C3 carbide transformation in Fe–Cr–Ni–C HP type alloy
  Acta Materialia, 2015
• Carburization of high chromium alloys
  Materials and Corrosion, 1998
• Niobium additions in HP heat-resistant cast stainless steels
  Materials Characterization, 1992
• Carburization kinetics of heat-resistant steels
  Oxidation of Metals, 1982