Evaluation of brake parameters in copper discs of various thicknesses and speeds using Neodymium – Iron – Boron Magnets

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Neodymium – Iron – Boron (NdFeB) permanent magnets of 12.5 mm thickness and 50 mm diameter are chosen for analyses because of their higher remanence and coercivity. Experimental analyses were carried out with Copper discs of thickness 4 mm, 6 mm and 8 mm at 2000 rpm, 3000 rpm, 4000 rpm and 5000 rpm. Experiments were conducted with three different positions of magnets such as 2 coaxial magnets, single magnet and single magnet with sudden application conditions. The brake parameters recorded are % speed reduction, deceleration and time taken. In 2 coaxial magnets condition, brake parameters are better in 6 mm thick disc. In single magnet condition, the brake parameters in 6 mm thick disc are found to be more consistent than 4 mm and 8 mm thick discs. In single magnet with sudden application condition, in 4 mm thick disc, the brake parameters are found better. During analysis, very high repulsion was experienced by magnet with 8 mm thick Copper disc at all the above mentioned speeds in single magnet with sudden application condition. For high speed train applications, single magnet condition with 6mm thick disc may be suitable. For high speed automotive applications, single magnet with sudden application condition with 4 mm thick disc may be suitable.

This publication has 6 references indexed in Scilit: