Microstructure, hardness and residual stress distribution in maraging steel gas tungsten arc weldments

Authors:
  • PRP. Venkata Ramana
    P. Venkata Ramana
  • GRG. Madhusudhan Reddy
    G. Madhusudhan Reddy
  • TMT. Mohandas
    T. Mohandas
Publisher website
Google Scholar
Abstract
The distribution of residual stresses due to welding has been studied in maraging steel welds. Gas tungsten arc welding process was used and the effect of filler metal composition on the nature of residual stress distribution has been investigated using X-ray diffraction technique with Cr Kα radiation. Three types of filler materials were used, they include: maraging filler, austenitic stainless steel and medium alloy medium carbon steel filler metal. In the case of maraging steel weld, medium alloy medium carbon filler, the residual stress at the centre of the weld zone was more compressive while, less compressive stresses have been identified in the heat affected zone of the parent metal adjacent to the weld metal. But, in the case of austenitic stainless steel filler the residual stresses at the centre of the weld and heat affected zone were tensile. Post-weld aging treatment reduced the magnitude of stresses. The observed residual stress distribution across the weldments has been correlated with microstructure and hardness distribution across the weld.

This publication has 13 references indexed in Scilit: