Study of the Effect of the A206/1.0 wt. % γAl2O3 Nanocomposites Content on the Portevin-Le Chatelier Phenomenon in Al/0.5 wt. % Mg Alloys

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The Portevin-Le Chatelier (PLC) phenomenon or dynamic strain aging in Al–0.5 wt. % Mg alloys was investigated at different strain rates. This research also examined the effect of γAl2O3 nanoparticles on the PLC phenomenon. A nanocomposite made of A206/1.0 wt. % γAl2O3 was manufactured to this purpose and then, added to an Al–0.5 wt. % Mg melt to obtain ingots of Al–0.5 wt. % Mg–20 wt. % A206/1.0 wt. % γAl2O3 and Al–0.5 wt. % Mg–10 wt. % A206/1.0 wt. % γAl2O3 with 6 mm diameter. Cold deformation allowed manufacturing 1 mm diameter wires using the 6 mm diameter ingots. A 300 °C solution treatment, followed by rapid cooling in ice water permitted to retain Mg atoms in solid solution. The tensile tests performed on the wires revealed the PLC phenomenon upon the tensile stress vs. strain plastic zone. The phenomenon was quantified using MatLab™ and statistical analysis. The results demonstrated how the alumina nanoparticles can diminish the serration amplitude of the PLC phenomenon.
Funding Information
  • National Science Foundation (1345156)

This publication has 20 references indexed in Scilit: