Nanopillar Templating Augments the Stiffness and Strength in Biopolymer Films

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Natural load-bearing mammalian tissues, such as cartilage and ligaments, contain ∼70% water yet can be mechanically stiff and strong due to the highly templated structures within. Here, we present a bioinspired approach to significantly stiffen and strengthen biopolymer hydrogels and films through the combination of nanoscale architecture and templated microstructure. Imprinted submicrometer pillar arrays absorb energy and deflect cracks. The produced chitosan hydrogels show nanofiber chains aligned by nanopillar topography, subsequently templating the microstructure throughout the film. These templated nanopillar chitosan hydrogels mechanically outperform unstructured flat hydrogels, with increases in the moduli of ∼160%, up to ∼20 MPa, and work at break of ∼450%, up to 8.5 MJ m–3. Furthermore, the strength at break increases by ∼350%, up to ∼37 MPa, and it is one of the strongest hydrogels yet reported. The nanopillar templating strategy is generalizable to other biopolymers capable of forming oriented domains and strong interactions. Overall, this process yields hydrogel films that demonstrate mechanical performance comparable to that of other stiff, strong hydrogels and natural tissues.
Funding Information
  • Congressionally Directed Medical Research Programs (W81XWH-17- 0355)

This publication has 58 references indexed in Scilit: