Polymer-Derived Carbon Matrix Composites with Boron Nitride Nanotube Reinforcement

Authors:
Open Access
Publisher website
Google Scholar
Abstract
This study explored the use of boron nitride nanotubes (BNNTs) as reinforcing fillers to enhance the mechanical properties of polymer-derived carbon matrix composites. BNNT-reinforced carbon matrix composites containing 0.5–5 wt% BNNTs were fabricated with pyrolysis conducted at different temperatures. X-ray diffraction and Raman spectroscopy revealed enhanced crystallinity and reduced defects in carbon matrix composites with BNNT addition. At 1200 °C pyrolysis temperature, sample shrinkage decreased from 28% in the control sample without BNNT addition to 12% with 5 wt% BNNTs, demonstrating BNNTs’ significant influence on the matrix. The density increased by 20.1% with 5 wt% BNNTs. Mechanical testing demonstrated an enhancement in the failure strain from 0.7% to 0.8% and an 87.8% increase in the work of fracture with 5 wt% BNNTs. Furthermore, the flexural strength and modulus improved by 68.7% and 55.6%, respectively, at this BNNT concentration. Increasing the pyrolysis temperature to 1500 °C further boosted the mechanical properties, with the flexural strength increasing by 283.7% and the flexural modulus by 528.6% when comparing samples containing 5 wt% BNNTs to those without BNNT reinforcement. Samples processed at 1500 °C with 5 wt% BNNT composition exhibited optimal performance.
Funding Information
  • National Science Foundation under award (#2302478)

This publication has 60 references indexed in Scilit: