Synergistic Enhancement of Stain Resistance in Exterior Wall Coatings Using SiO2-TiO2 Composite Overlay

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Architectural exterior wall coatings require a balance of elasticity, stain resistance, and durability. Although nano-SiO2 enhances fracture resistance in elastic coatings, its limited hydrophobicity allows pollutant adhesion. Nano-TiO2 can photocatalytically degrade organics but is often encapsulated by the polymer matrix, reducing its effectiveness. This study introduces a SiO2-TiO2 composite topcoat applied via aqueous dispersion to overcome these limitations. Experimental results demonstrate that the composite coating significantly outperforms single-component modifications, improving stain resistance by 21.3% after 12 months of outdoor exposure. The surface remains brighter with markedly reduced pollutant accumulation. Mechanistically, SiO2 serves as an inert mesoporous carrier that improves the dispersion and photostability of TiO2, minimizing agglomeration and photocorrosion. Its inherent hardness and hydrophobicity reduce physical adsorption sites. Together, SiO2 and TiO2 create a nanoscale rough surface that enhances hydrophobicity through a lotus-like effect. Under UV irradiation, TiO2 generates radicals that decompose organic pollutants and inhibit microbial growth, enabling efficient self-cleaning with rainwater. This synergistic mechanism addresses the limitations of individual nanoparticles, successfully integrating elasticity with long-term anti-fouling and durability. This composite demonstrates a significant advancement in stain resistance and overall durability, offering potential applications in energy-efficient and environmentally sustainable building technologies.
Funding Information
  • Natural Science Foundation of Jiangxi (20232BAB204105, 20224BAB214041)
  • Xinyu University Education Reform Project (XJJG-24-2)
  • Undergraduate Course Construction Project for Cooperation between Universities and Enterprises “Civil Engineering Materials”

This publication has 17 references indexed in Scilit: