The early-age cracking sensitivity, shrinkage, hydration process, pore structure and micromechanics of cement-based materials containing alkalis with different metal ions

This publication has 34 references indexed in Scilit:

• Nanoscale insights into the interfacial characteristics between calcium silicate hydrate and silica
  Applied Surface Science, 2023
• Susceptibility of Portland cement and blended cement concretes to plastic shrinkage cracking
  Cement and Concrete Composites, 2018
• Microstructural and bulk property changes in hardened cement paste during the first drying process
  Cement and Concrete Research, 2014
• The effect of drying on early-age morphology of C–S–H as observed in environmental SEM
  Cement and Concrete Research, 2010
• Drying and autogenous shrinkage of pastes and mortars with activated slag cement
  Cement and Concrete Research, 2008
• Refinements to colloid model of C-S-H in cement: CM-II
  Cement and Concrete Research, 2008
• Influence of alkali on restrained shrinkage behavior of cement-based materials
  Cement and Concrete Research, 2005
• On the use of nanoindentation for cementitious materials
  Materials and Structures, 2003
• On the reaction of C-S-H(di, poly) with alkali hydroxides
  Cement and Concrete Research, 1989
• The release of alkalis from pulverised-fuel ashes and ground granulated blastfurnace slags in the presence of Portland cements
  Cement and Concrete Research, 1988