CURING EFFECTIVENESS OF SINGLE-PEAK AND MULTI-PEAK LED LIGHT CURING UNITS ON TPO-CONTAINING RESIN COMPOSITES WITH DIFFERENT CHROMATIC CHARACTERISTICS

Author:
Publisher website
Google Scholar
Abstract
This study evaluated the surface microhardness of Lucirin-TPO (TPO) containing resin based composite (RBC) cured with three light-emitting diode (LED) light curing units (LCUs) (two single-peak LED and one multi-peak LED), and two different energy density (ED) (8 J/cm2 and 16 J/cm2). Ninety specimens (8 mm wide and 2 mm thick) (n=5), were prepared with three different shades: translucent (T), A2 dentin (A2d), and A4 dentin (A4d). Specimens were subjected to micro-hardness Vickers measurements (Vickers Hardness Number, VHN) on both top and bottom surfaces. Hardness ratio (rHV) was also calculated. Data were analyzed using multifactorial ANOVA and Bonferroni tests (<=0.05). Results indicated that higher ED performed better than lower ED. Multi-peak LED achieved higher VHNs and rHV than single-peak LED when curing a TPO-containing RBC. A4d invariably achieved lower rHV and VHN than T and A2d. Single-peak LED achieved comparable VHNs and rHVs with multi-peak LED only curing A2d and T shades with 16J/cm2.

This publication has 59 references indexed in Scilit: