PERFORMANCE ENHANCEMENT OF BRASS EDM ELECTRODES WITH CRYOGENIC TREATMENT WHILE MACHINING THE COLD WORK STEEL AISI D2

Authors:
Publisher website
Google Scholar
Abstract
This study investigates the performance of deep cryogenically treated brass (CuZn25Al5) electrodes in the die-sink EDM process. Two different cryogenic treatment durations, 6[ ]h and 12[ ]h, were applied to 8[ ]mm diameter electrodes, and their effects were compared to untreated electrodes. The machining tests were conducted under moderate and aggressive conditions. In the machining tests, the 6-h cryo-treated electrode exhibited a 16.8% increase in material removal rate (MRR) under moderate conditions and a 19.7% increase under aggressive conditions compared to the reference electrode. The 12-h cryo-treated electrode showed similar MRR values to the reference electrode but improved tool wear resistance by 9.4% under moderate conditions. The kerf angle was minimized, indicating better hole verticality, in the 6-h cryo-treated electrode group. The improvement in machining performance was attributed to the enhancement in electrical conductivity of the electrodes, which increased by 28% for the 6-h cryo-treated electrode and 20% for the 12-h cryo-treated electrode. X-ray diffraction (XRD) analysis revealed shifts in peak positions and possible phase transformations due to cryogenic treatment. Surface roughness measurements showed improved surface conditions in the cryo-treated electrodes under aggressive conditions. The results indicate that cryogenic treatment enhances MRR, reduces tool wear, and improves surface quality in die-sink EDM. These improvements are attributed to increased electrical conductivity and changes in the internal structure of the brass electrode.

This publication has 34 references indexed in Scilit: