Low-Temperature Microwave Annealing Processes for Future IC Fabrication—A Review
- 19 February 2014
- journal article
- review article
- Published by Institute of Electrical and Electronics Engineers (IEEE) in IEEE Transactions on Electron Devices
- Vol. 61 (3) , 651-665
Abstract
Microwave annealing (MWA) and rapid thermal annealing (RTA) of dopants in implanted Si are compared in their abilities to produce very shallow and highly activated junctions. First, arsenic (As), phosphorus (P), and BF2 implants in Si substrate were annealed by MWA at temperatures below 550 °C. Next, enhancing the substitutional carbon concentration ([C]sub) by cluster carbon implantation in (100) Si substrates with MWA or RTA techniques was investigated. Annealing temperatures and time effects were studied. Different formation mechanisms of SiCx layer were observed. In addition, substrate temperature is an important factor for dopant activation during MWA and in situ doped a-Si on oxide/Si substrate or glass were compared to elucidate the substrate temperature effect. After the discussion of dopant activation in Si substrates, low temperature formation of ultrathin NiGe layer is presented. Ultrathin NiGe films with low sheet resistance have been demonstrated with a novel two-step MWA process. In the two-step MWA process, the first step anneals the sample with low power MWA, and the second step applies higher power MWA for reducing sheet resistance. During fixed-frequency microwave heating, standing wave patterns may be present in the MWA chamber resulting in nodes and antinodes and thermal variations over the process wafer. Therefore, the effects of Si or quartz susceptor wafers on dopant activation and sheet resistance uniformity during fixed-frequency MWA were investigated.Keywords
This publication has 32 references indexed in Scilit:
- Carbon Incorporation into Substitutional Silicon Site by Molecular Carbon Ion Implantation and Recrystallization Annealing as Stress Technique in n-Metal–Oxide–Semiconductor Field-Effect TransistorJapanese Journal of Applied Physics, 2010
- Enhancing CMOS transistor performance using lattice-mismatched materials in source/drain regionsSemiconductor Science and Technology, 2006
- Microwaves in organic synthesis. Thermal and non-thermal microwave effectsChemical Society Reviews, 2005
- Controlled Microwave Heating in Modern Organic SynthesisAngewandte Chemie International Edition, 2004
- Electromagnetic fast firing for ultrashallow junction formationIEEE Transactions on Semiconductor Manufacturing, 2003
- Temperature-resolved, in-situ powder X-ray diffraction of silver iodide under microwave irradiationPhysChemComm, 2002
- Thermal processing of silicon wafers with microwave co-heatingMicroelectronic Engineering, 2000
- Microwave enhanced reaction kinetics in ceramicsMaterials Research Innovations, 1997
- Topics in solid phase epitaxy: Strain, structure and geometryMaterials Science and Engineering: R: Reports, 1996
- Mechanisms for nonthermal effects on ionic mobility during microwave processing of crystalline solidsJournal of Materials Research, 1992