Effect of cellulose acetate/cellulose triacetate ratio on reverse osmosis blend membrane performance

Authors:
Publisher website
Google Scholar
Abstract
Surface functionalization and modification including the grafting process are effective approaches to improve and enhance the reverse osmosis (RO) membrane performance. This work is aimed to synthesize grafted/crosslinked cellulose acetate (CA)/cellulose triacetate (CTA) blend RO membranes using N‐isopropylacrylamide (N‐IPAAm) as a monomer and N,N‐methylene bisacrylamide (MBAAm) as a crosslinker. The morphology of these membranes was analyzed by scanning electron microscopy and their surface roughness was characterized by atomic force microscopy. The performance of these membranes was evaluated through measuring two major parameters of salt rejection and water flux using RO unit at variable operating pressures. It was noted that the surface average roughness obviously decreased from 148 nm for the pure CA/CTA blend membrane with 2.5% CTA to 110 nm and 87 nm for the grafted N‐IPAAm and grafted/crosslinked N‐IPAAM/MBAAm/CA/CTA‐RO membranes, respectively. Moreover, the contact angle decreased from 51.98° to 47.6° and 43.8° after the grafting and crosslinking process. The salt rejection of the grafted CA/CTA‐RO membrane by 0.1% N‐IPAAm produced the highest value of 98.12% and the water flux was 3.29 L/m2h at 10 bar.

This publication has 40 references indexed in Scilit: