Electrochemical and Structural Study of a Chemically Dealloyed PtCu Oxygen Reduction Catalyst

Authors:
Publisher website
Google Scholar
Abstract
A carbon-supported, dealloyed platinum−copper (Pt−Cu) oxygen reduction catalyst was prepared using a multistep synthetic procedure. Material produced at each step was characterized using high-angle annular dark-field scanning transmission electron microscopy, electron energy loss spectroscopy mapping, X-ray absorption spectroscopy, X-ray diffraction, and cyclic voltammetry, and its oxygen reduction reaction (ORR) activity was measured by a thin-film rotating disk electrode technique. The initial synthetic step, a coreduction of metal salts, produced a range of poorly crystalline Pt, Cu, and Pt−Cu alloy nanoparticles that nevertheless exhibited good ORR activity. Annealing this material alloyed the metals and increased particle size and crystallinity. Transmission electron microscopy shows the annealed catalyst to include particles of various sizes, large (>25 nm), medium (12−25 nm), and small (<12 nm). Most of the small and medium-sized particles exhibited a partial or complete core−shell (Cu-rich core and Pt shell) structure with the smaller particles typically having more complete shells. The appearance of Pt shells after annealing indicates that they are formed by a thermal diffusion mechanism. Although the specific activity of the catalyst material was more than doubled by annealing, the concomitant decrease in Pt surface area resulted in a drop in its mass activity. Subsequent dealloying of the catalyst by acid treatment to partially remove the copper increased the Pt surface area by changing the morphology of the large and some medium particles to a “Swiss cheese” type structure having many voids. The smaller particles retained their core−shell structure. The specific activity of the catalyst material was little reduced by dealloying, but its mass activity was more than doubled due to the increase in surface area. The possible origins of these results are discussed in this report.

This publication has 46 references indexed in Scilit: