The Effect of Irradiation Dose and Temperature on Irradiation Hardening and Microstructure Study of Hot-Forged V-4Cr-4Ti Under Self-Ion Irradiation

Authors:
Open Access
Publisher website
Google Scholar
Abstract
After being self-ion implanted at 400 °C and 550 °C, the microstructure and irradiation hardness of kilogram-scale V-4Cr-4Ti alloys were studied using a transmission electron microscope (TEM) and nano-indentation test technology. Irradiation was performed using self-ions (V2+) at 2.5 MeV with design influences of 1.15 × 1015 ions cm−2, 4.59 × 1015 ions cm−2, and 9.17 × 1015 ions cm−2, so that the peak damages of V-4Cr-4Ti alloys are 1, 4, and 8 dpa, respectively. Compared with the 400 °C samples, the 550 °C samples exhibited a higher-density number of dislocation loops and increased hardness and reached saturation at lower irradiation doses. The irradiation temperature was mainly responsible for these differences, and the potential mechanism for its effect on the irradiation behavior was discussed.
Funding Information
  • National Natural Science Foundation of China (No. 12175028, No. 12275073, No. 202301XWCX004-02)
  • Innovation Program of Southwestern Institute of Physics (No. 12175028, No. 12275073, No. 202301XWCX004-02)

This publication has 32 references indexed in Scilit: