In SituStudy of Atomic Structure Transformations of Pt–Ni Nanoparticle Catalysts during Electrochemical Potential Cycling

Authors:
Publisher website
Google Scholar
Abstract
When exposed to corrosive anodic electrochemical environments, Pt alloy nanoparticles (NPs) undergo selective dissolution of the less noble component, resulting in catalytically active bimetallic Pt-rich core–shell structures. Structural evolution of PtNi6 and PtNi3 NP catalysts during their electrochemical activation and catalysis was studied by in situ anomalous small-angle X-ray scattering to obtain insight in element-specific particle size evolution and time-resolved insight in the intraparticle structure evolution. Ex situ high-energy X-ray diffraction coupled with pair distribution function analysis was employed to obtain detailed information on the atomic-scale ordering, particle phases, structural coherence lengths, and particle segregation. Our studies reveal a spontaneous electrochemically induced formation of PtNi particles of ordered Au3Cu-type alloy structures from disordered alloy phases (solid solutions) concomitant with surface Ni dissolution, which is coupled to spontaneous residual Ni metal segregation during the activation of PtNi6. Pt-enriched core–shell structures were not formed using the studied Ni-rich nanoparticle precursors. In contrast, disordered PtNi3 alloy nanoparticles lose Ni more rapidly, forming Pt-enriched core–shell structures with superior catalytic activity. Our X-ray scattering results are confirmed by STEM/EELS results on similar nanoparticles.

This publication has 47 references indexed in Scilit: