Upshift of Phase Transition Temperature in Nanostructured PbTiO3 Thick Film for High Temperature Applications

Authors:
Publisher website
Google Scholar
Abstract
Thick polycrystalline pure PbTiO3 films with nano size grains were synthesized for the first time by aerosol deposition. Annealed 7 μm thick films exhibit well-saturated ferroelectric hysteresis loops with a remanent polarization and coercive field of 35 μC/cm2 and 94 kV/cm, respectively. A large-signal effective d33,eff value of >60 pm/V is achieved at room temperature. The measured ferroelectric transition temperature (Tc) of the films ∼550 °C is >50 °C higher than the reported values (∼490 °C) for PbTiO3 ceramics. First-principles calculations combined with electron energy loss spectroscopy (EELS) and structural analysis indicate that the film is composed of nano size grains with slightly decreased tetragonality. There is no severe off-stoichiometry, but a high compressive in-plane residual stress was observed in the film along with a high transition temperature and piezoelectric response. The ferroelectric characteristics were sustained until 200 °C, providing significant advancement toward realizing high temperature piezoelectric materials.
Funding Information
  • Inha University
  • National Research Foundation of Korea (2011-0010905, 2012R1A1A2A10041947)
  • Ministry of Science, ICT and Future Planning (2010-0019317, 2013-073298)

This publication has 40 references indexed in Scilit: