Functionalized Few-Walled Carbon Nanotubes for Mechanical Reinforcement of Polymeric Composites
Authors:
- 27 April 2009
- journal article
- research article
- Published by American Chemical Society (ACS) in ACS Nano
- Vol. 3 (5) , 1057-1062
Abstract
Compared to single-walled carbon nanotubes (SWNTs) and more defective multiwalled carbon nanotubes (MWNTs), the thin few-walled carbon nanotubes (FWNTs) are believed to have extraordinary mechanical properties. However, the enhancement of mechanical properties in FWNTs-polymer composites has remained elusive. In this study, free-standing carbon nanotubes (CNTs)/polymer composite films were fabricated with three types (SWNTs, FWNTs, MWNTs) of functionalized CNTs. The mechanical properties of composite films have been investigated. It is observed that the Young’s modulus of composite films with only 0.2 wt % functionalized FWNTs shows a remarkable reinforcement value of dY/dVf = 1658 GPa, which is ∼400 GPa higher than the highest value (dY/dVf = 1244 GPa) that was previously reported. In addition, the Young’s modulus increased steadily with the increased concentration of FWNTs. The results indicated that FWNTs are practically the optimum reinforcing filler for the next generation of carbon nanotube-based composite materials.Keywords
This publication has 28 references indexed in Scilit:
- Synthesis of High-Purity Few-Walled Carbon Nanotubes from Ethanol/Methanol MixtureChemistry of Materials, 2006
- Mechanical Reinforcement of Polymers Using Carbon NanotubesAdvanced Materials, 2006
- Mechanical Properties of Functionalized Single‐Walled Carbon‐Nanotube/Poly(vinyl alcohol) NanocompositesAdvanced Functional Materials, 2005
- Nanocomposites in contextComposites Science and Technology, 2005
- Mechanical Property Characterization of a Polymeric Nanocomposite Reinforced by Graphitic Nanofibers with Reactive LinkersJournal of Composite Materials, 2004
- Poly(vinyl alcohol)/SWNT Composite FilmNano Letters, 2003
- Fiber waviness in nanotube-reinforced polymer composites—I: Modulus predictions using effective nanotube propertiesComposites Science and Technology, 2003
- Fiber waviness in nanotube-reinforced polymer composites—II: modeling via numerical approximation of the dilute strain concentration tensorComposites Science and Technology, 2003
- Morphological and mechanical properties of carbon-nanotube-reinforced semicrystalline and amorphous polymer compositesApplied Physics Letters, 2002
- Exceptionally high Young's modulus observed for individual carbon nanotubesNature, 1996