Solvent-Free Method of Polyacrylonitrile-Coated LLZTO Solid-State Electrolytes for Lithium Batteries

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Solid-state electrolytes (SSEs), particularly garnet-type Li6.4La3Zr1.4Ta0.6O12 (LLZTO), offer high stability and a wide electrochemical window. However, their grain boundaries limit ionic conductivity, necessitating high-temperature sintering for improved performance. Yet, this process results in brittle electrolytes prone to fracture during manufacturing. To address these difficulties, solvent-free solid-state electrolytes with a polyacrylonitrile (PAN) coating on LLZTO particles are reported in this work. Most notably, the PAN-coated LLZTO (PAN@LLZTO) electrolyte demonstrates self-supporting characteristics, eliminating the need for high-temperature sintering. Importantly, the homogeneous polymeric PAN coating, synthesized via the described method, facilitates efficient Li+ transport between LLZTO particles. This electrolyte not only achieves an ionic conductivity of up to 2.11 × 10−3 S cm−1 but also exhibits excellent interfacial compatibility with lithium. Furthermore, a lithium metal battery incorporating 3% PAN@LLZTO-3%PTFE as the solid-state electrolyte and LiFePO4 as the cathode demonstrates a remarkable specific discharge capacity of 169 mAh g−1 at 0.1 °C. The strategy of organic polymer-coated LLZTO provides the possibility of a green manufacturing process for preparing room-temperature sinter-free solid-state electrolytes, which shows significant cost-effectiveness.
Funding Information
  • Jilin Province Industry Key Core Technology Research Project (20240302101GX)

This publication has 41 references indexed in Scilit: