Role of Localized States in Photoluminescence Dynamics of High Optical Gain CsPbBr3 Nanocrystals

Authors:
Publisher website
Google Scholar
Abstract
Temperature‐dependent time‐resolved photoluminescence (TRPL) spectroscopy of high optical gain CsPbBr3 nanocrystals (NCs) films along with temperature‐dependent steady‐state absorption and photoluminescence (PL) spectra is studied. A red shift in the optical band edge and the corresponding PL peak is observed by lowering the temperature from room temperature, analogous to hybrid perovskite semiconductors. However, the faster PL decay of CsPbBr3 NCs film at a low temperature as compared to room temperature is in contrast with many other traditional colloidal quantum dots. The TRPL spectroscopy as a function of temperature suggests the presence of a red‐shifted (≈75 ± 15 meV) defect‐induced emission peak at longer times. Temperature‐dependent PL intensity study shows an Arrhenius type of character with two activation energies: ≈77 ± 18 and ≈12 ± 3 meV. A qualitative model is developed where interaction between the excitonic level and these observed localized states as a function of temperature can qualitatively explain the contrasting PL decay mechanism of CsPbBr3 NCs film. To ensure the quality of in‐house synthesized CsPbBr3 NCs with a mixture of oleylamine and octylamine ligands, the amplified spontaneous emission from CsPbBr3 NCs film as a planar waveguide medium is studied, which shows state‐of‐art optical gain coefficient of ≈51cm−1 and a loss coefficient of ≈15cm−1 at room temperature.
Funding Information
  • Indian Institute of Technology Bombay (12IRCCSG044)
  • Anusandhan National Research Foundation (DST/TM/SERI/FR/186(G))

This publication has 47 references indexed in Scilit: