Crystallization Process for Superionic Li 7 P 3 S 11 Glass–Ceramic Electrolytes
- 24 March 2011
- journal article
- Published by Wiley in Journal of the American Ceramic Society
- Vol. 94 (6) , 1779-1783
Abstract
The crystallization process of the 70Li 2 S·30P 2 S 5 (mol%) glass was investigated to obtain a guideline for enhancing the crystallinity of Li 7 P 3 S 11 crystals in a glass–ceramic. Results show that the glass softened at around 240°C and that surface crystallization of the glass started at around 250°C. The heat‐treatment conditions with a maximum nucleation rate for the glass were estimated using DSC measurements. The glass–ceramic prepared using two‐step heat treatment of 210°C for 30 min (nucleation) and 280°C for 1 h (crystallization) exhibited high conductivity of 5.2 × 10 −3 S/cm at room temperature.Keywords
This publication has 11 references indexed in Scilit:
- Controlled crystallization and ionic conductivity of a nanostructured LiAlGePO4 glass–ceramicJournal of Non-Crystalline Solids, 2009
- Preparation of lithium ion conducting glasses and glass–ceramics for all-solid-state batteriesJournal of Non-Crystalline Solids, 2008
- Crystal structure of a superionic conductor, Li7P3S11Solid State Ionics, 2007
- Lithium ion conductivity of the Li2S–P2S5 glass-based electrolytes prepared by the melt quenching methodSolid State Ionics, 2007
- New, Highly Ion‐Conductive Crystals Precipitated from Li2S–P2S5 GlassesAdvanced Materials, 2005
- Preparation of Li 2 S–P 2 S 5 Amorphous Solid Electrolytes by Mechanical MillingJournal of the American Ceramic Society, 2001
- Electrochemical Properties for the Lithium Ion Conductive (100‐x ) ( 0.6Li2 S · 0.4SiS2 ) · xLi4SiO4 Oxysulfide GlassesJournal of the Electrochemical Society, 1999
- Mechanochemical Synthesis of New Amorphous Materials of 60Li 2 S·40SiS 2 with High Lithium Ion ConductivityJournal of the American Ceramic Society, 1999
- Kinetic study of crystallization of glass by differential thermal analysis—criterion on application of Kissinger plotJournal of Non-Crystalline Solids, 1980
- Reaction Kinetics in Differential Thermal AnalysisAnalytical Chemistry, 1957