Modification of Surface Properties of Colloidal Suspensions of NixOy-SiO2 Mixed Oxides with Different Ni Contents by the Adsorption Layers of Poly(Vinyl Alcohol)

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The adsorption and electrokinetic properties of hybrid silica materials composed of nickel and silicon oxides (NixOy-SiO2), characterized by different contents of nickel oxide (from 0.5 to 3 mmol/g SiO2), were examined. These solids were also modified by poly(vinyl alcohol) to change their surface characteristics. The polymer is non-toxic and very well soluble in water. Due to incomplete hydrolysis of the polymer acetate groups, its macromolecules become negatively charged. The limited range of studied pH (6–10) resulted from high solubility of nickel oxide at more acidic pH values. The spectrophotometric, surface charge and electrophoretic measurements indicated that PVA exhibits higher adsorption affinity for the surfaces of mixed oxide with a larger content of nickel in its structure. Moreover, the presence of polymeric layers on the solid surface influences considerably the structure of electrical double layer formed at the mixed oxide-aqueous solution interface.
Funding Information
  • Maria Curie-Sklodowska University in Lublin

This publication has 40 references indexed in Scilit: