Investigation of Weld Formation, Microstructure and Mechanical Properties of Small Core Diameter Single Mode Fiber Laser Welding of Medium Thick 6061 Aluminum Alloy

Authors:
Open Access
Publisher website
Google Scholar
Abstract
In this study, a small core diameter single mode fiber laser was applied to weld an 8 mm thick plate of 6061-T6 aluminum alloy. The microstructural evolution and mechanical properties of the laser welded aluminum alloy specimens were investigated in detail. The results indicated that fully penetrated welded specimens, free of welding defects like porosity, melt sagging, and hot cracking could be achieved by optimizing the processing parameters through response surface methodology. The upper part of the fusion zone consisted mainly of fine equiaxed dendrites, with secondary dendrite arm spacing (SDAS) of approximately 3–5 μm. While the lower region of the fusion zone exhibited pronounced microstructural coarsening, made up mostly of coarse columnar grains, along with some localized equiaxed grains, and an SDAS ranging from 8 to 12 μm. Both the fusion zone and heat affected zone (HAZ) were characterized by a “softened” hardness profile. The fusion zone featured a narrow region with the lowest microhardness across the welded joint with the microhardness value reducing to ~72% of the base metal (BM). Meanwhile, the microhardness of the HAZ was ~87.4% of the BM. The ultimate tensile strength of laser welded specimens was ~243.6 MPa, amounting to approximately 78.3% of the base metal. This study provides a fresh approach for welding medium-thick aluminum alloy plate using a high-quality laser beam, even at the kilowatt level with a fiber laser, and it shows a strong promise for applications in light-alloy manufacturing sectors such as automotive, rail transportation, aerospace, and beyond.

This publication has 33 references indexed in Scilit: