Mechanical Characterizations of 3D-printed PLLA/Steel Particle Composites
Open Access
Abstract
The objective of this study is to characterize the micromechanical properties of poly-l-lactic acid (PLLA) composites reinforced by grade 420 stainless steel (SS) particles with a specific focus on the interphase properties. The specimens were manufactured using 3D printing techniques due to its many benefits, including high accuracy, cost effectiveness and customized geometry. The adopted fused filament fabrication resulted in a thin interphase layer with an average thickness of 3 µm. The mechanical properties of each phase, as well as the interphase, were characterized by nanoindentation tests. The effect of matrix degradation, i.e., imperfect bonding, on the elastic modulus of the composite was further examined by a representative volume element (RVE) model. The results showed that the interphase layer provided a smooth transition of elastic modulus from steel particles to the polymeric matrix. A 10% volume fraction of steel particles could enhance the elastic modulus of PLLA polymer by 31%. In addition, steel particles took 37% to 59% of the applied load with respect to the particle volume fraction. We found that degradation of the interphase reduced the elastic modulus of the composite by 70% and 7% under tensile and compressive loads, respectively. The shear modulus of the composite with 10% particles decreased by 36%, i.e., lower than pure PLLA, when debonding occurred.Keywords
This publication has 35 references indexed in Scilit:
- 3D printing of thermoplastic PI and interlayer bonding evaluationMaterials Letters, 2018
- Effect of SiC/Al2O3particle size reinforcement in recycled LDPE matrix on mechanical properties of FDM feed stock filamentVirtual and Physical Prototyping, 2018
- Characterization of mechanical properties and fracture mode of additively manufactured carbon fiber and glass fiber reinforced thermoplasticsMaterials & Design, 2018
- 3D printing of polymer matrix composites: A review and prospectiveComposites Part B: Engineering, 2017
- Comparison of tribological behaviour for Nylon6-Al-Al2O3and ABS parts fabricated by fused deposition modellingVirtual and Physical Prototyping, 2015
- Mechanical, Electromagnetic, and X-ray Shielding Characterization of a 3D Printable Tungsten–Polycarbonate Polymer Matrix Composite for Space-Based ApplicationsJournal of Electronic Materials, 2015
- Thermo-mechanical properties of a highly filled polymeric composites for Fused Deposition ModelingMaterials & Design (1980-2015), 2011
- Effects of particle size, particle/matrix interface adhesion and particle loading on mechanical properties of particulate–polymer compositesComposites Part B: Engineering, 2008
- Interphase effect on the strengthening behavior of particle-reinforced metal matrix compositesComputational Materials Science, 2007
- Computational micromechanics of composites: The effect of particle spatial distributionMechanics of Materials, 2006