Direct Applicability of La0.6Sr0.4CoO3 – δ Thin Film Cathode to Yttria Stabilised Zirconia Electrolytes at T ≤ 650 °C

Authors:
Publisher website
Google Scholar
Abstract
For investigating the direct applicability of highly active cobalt containing cathodes on YSZ electrolytes at a lower processing and operating temperature range (T ≤ 650 °C), we fabricated a thin film lanthanum strontium cobalt oxide (LSC) cathode on an yttria stabilised zirconia (YSZ)‐based solid oxide fuel cell (SOFC) via pulsed laser deposition (PLD). Its electrochemical performance (5.9 mW cm–2 at 0.7 V, 650 °C) was significantly inferior to that (595 mW cm–2 at 0.7 V, 650 °C) of an SOFC with a thin (t ∼ 200 nm) gadolinium doped ceria (GDC) buffer layer in between the LSC thin film cathode and the YSZ electrolyte. It implies that even though the cathode processing and cell operating temperatures were strictly controlled not to exceed 650 °C, the direct application of LSC on YSZ should be avoided. The origin of the cell performance deterioration is thoroughly studied by glancing angle X‐ray diffraction (GAXRD) and transmission electron microscopy (TEM), and the decomposition of the cathode and diffusion of La and Sr into YSZ were observed when LSC directly contacted YSZ.

This publication has 28 references indexed in Scilit: