Hybrid low‐temperature sintering processes of electro‐ceramics

Authors:
Publisher website
Google Scholar
Abstract
Cold sintering process (CSP) developed recently has attracted much attention due to the ultralow sintering temperatures and high efficiencies with the assist of transient liquid phase (TLP). Based on CSP, we have further established a protocol for low‐temperature sintering processes by combining TLP with other sintering technologies, including hybrid sintering process with microwave and TLP (MW‐TLP), and hybrid sintering process with spark plasma sintering and TLP (SPS‐TLP). Three typical electro‐ceramics (TiO 2 , CaWO 4 , and ZnO) are selected, which are highly densified (>97%) with excellent electrical properties at reduced sintering temperatures, applied pressures or holding times, demonstrating the feasibility of MW‐TLP and SPS‐TLP in fabricating electro‐ceramics. Especially, the Q × f value of TiO 2 ceramics (38,020 GHz) prepared by MW‐TLP at 1000°C is 46.2% and 23.4% higher than that of microwave and spark plasma sintered samples, respectively, and comparable to traditional thermal sintered (TTS) samples at 1300–1400°C. The dielectric properties of MW‐TLP CaWO 4 ceramics sintered at 900°C for 2 h are comparable to TTS samples sintered at 1000–1300°C for 2–5 h. ZnO ceramics can be highly densified (∼98%) by SPS‐TLP with mild sintering conditions (200–300°C and 3.8–50 MPa) compared to SPS (>500°C) and CSP (>100 MPa). The frameworks of fundamental mechanisms are outlined together with the experimental data. It is expected that this work will provide promising sintering methods to fabricate electro‐ceramics and offer inspirations on sintering combinations to develop low‐temperature sintering processes with high efficiencies.
Funding Information
  • National Natural Science Foundation of China (51902245)

This publication has 85 references indexed in Scilit: