Ultrafast Synthesis of NASICON Solid Electrolytes for Sodium‐Metal Batteries

Authors:
Publisher website
Google Scholar
Abstract
NASICON‐structured solid‐state electrolytes (SSEs) are highly promising materials for sodium solid‐state metal batteries (NaSMBs). However, the current synthesis methods are often labor‐intensive and inefficient, consuming a significant amount of energy and time. Here, an ultrafast high‐temperature synthesis (UHS) technique is successfully demonstrated to directly synthesize NASICON‐type SSEs from mixed precursor powders, reducing the synthesis time from hours to merely seconds. The intermediate with a Na3PO4 structure plays a critical role in the rapid synthesis of NASICON‐type SSEs, ultimately leading to the formation of the final NASICON phase. Moreover, the UHS‐synthesizes NASICON‐type Na3.3Zr1.7Lu0.3Si2PO12 (NZLSP) exhibits high room temperature ionic conductivity of 7.7 × 10−4 S cm−1, approximately three times that of the undoped Na3Zr2Si2PO12 (NZSP). The Na|NZLSP|Na symmetric cell can sustain highly stable cycling for over 4800 h. This study provides a novel insight and validation in the precise and targeted synthesis of complex oxide solid‐state electrolytes.
Funding Information
  • National Natural Science Foundation of China (52272215, 52102313)

This publication has 63 references indexed in Scilit: