Fabrication of β -Ga 2 O 3 /ZnO heterojunction for solar-blind deep ultraviolet photodetection

Authors:
Publisher website
Google Scholar
Abstract
A thin-film type β -Ga 2 O 3 /ZnO heterojunction was constructed for the first time by radio frequency magnetron sputtering of a β -Ga 2 O 3 layer on a (0001) ZnO single crystalline substrate. The heterojunction presents a typical positive rectification in the dark, and shows a solar-blind deep ultraviolet photoelectric characteristic. Under zero bias, the photodetector based on a β -Ga 2 O 3 /ZnO heterojunction exhibits an I photo / I dark ratio of ∼14.8 under a 254 nm light illumination with a light intensity of 50 μ W cm −2 , showing a characteristic of working with zero power consumption. The photocurrent linear increases and the response time decreases with the increase of the light intensity. The photodetector shows a R λ of 0.35 A W −1 and an EQE of 1.7 × 10 2 % under 254 nm illumination of 50 μ W cm −2 and a negative bias of 5 V. This study presents a promising candidate for use in solar-blind deep ultraviolet photodetection.
Funding Information
  • Science Foundation of Zhejiang Sci-Tech University (16062190-Y)
  • Science and Technology Department of Zhejiang Province Foundation (2017C37017)
  • National Natural Science Foundation of China (51572033)

This publication has 18 references indexed in Scilit: