Synthesis and evaluation of nickel doped Co3O4 produced through hydrothermal technique

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The synthesis of undoped cobalt oxide and cobalt oxide with 4%nickel doping is studied in samples obtained through hydrothermal technique. After the final heat treatment at 300°C, X-ray diffraction analysis indicated the formation of cobalt spinel oxide with a complete replacement of nickel in the lattice. An average crystallite size of ~42 nm and ~31nm was found, as well as a particle size of ~ 20 nm and ~30 nm for Co3O4 and Co3-xNixO4, respectively. Structural parameters were established through Rietveld refinement with a good correspondence between the simulated and the experimental pattern with values of x2 = 1.25 and GOF = 0.90 for Co3O4. The energy band gap was found through UV-Vis spectroscopy in two different regions: Eg1 and Eg2 values vary between 1.54 and 2.04eV for samples doped with nickel. The SEM results indicated the formation of nanostructures with semi-cubic shape and irregular rods. Parameters such as crystal size, particle size, surface area, as well as morphology of the final product depend on doping.

This publication has 32 references indexed in Scilit: