In-Service Degradation of Mechanical Characteristics of Pipe Steels in Gas Mains

This publication has 22 references indexed in Scilit:

• Analysis and mechanical properties characterization of operated gas main elbow with hydrogen assisted large-scale delamination
  Engineering Failure Analysis, 2017
• Corrosion Degradation of Steel of an Elbow of Gas Pipeline with Large-Scale Delamination after Long-Term Operation
  Materials Science, 2017
• Effect of long-term operation on steels of main gas pipeline. Reduction of static fracture toughness
  Journal of Natural Gas Science and Engineering, 2017
• Diagnostic Indications of the In-Service Degradation of the Pressure Regulator of a Gas-Transportation System
  Materials Science, 2016
• Fractographic Signs of the Mechanisms of Transportation of Hydrogen in Structural Steels
  Materials Science, 2016
• Diagnostics of Hydrogen Macrodelamination in the Wall of a Bent Pipe in the System of Gas Mains
  Materials Science, 2016
• Fractographic Signs of the In-Service Degradation of Welded Joints of Oil Mains
  Materials Science, 2015
• The mechanism of failure by hydrogen induced cracking in an acidic environment for API 5L X70 pipeline steel
  International Journal of Hydrogen Energy, 2015
• Computer analysis of characteristic elements of fractographic images
  Materials Science, 2013
• Effect of long-term service on the tensile properties and capability of pipeline steel 17GS to resist cleavage fracture
  International Journal of Pressure Vessels and Piping, 2004