Effects of Nonmagnetic Zn2+ Ion and RE Ion Substitution on the Magnetic Properties of Functional Nanomaterials Co1−yZnyRExFe2−xO4 (RE = La, Sm, Gd) by Sol–Gel

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Magnetic Functional Nanomaterials Co1−yZnyRExFe2−xO4 (RE (rare-earth) = La,Sm,Gd) were prepared using the sol–gel combustion method. XRD characterization confirms that the ferrite samples we synthesized are single-phase cubic structures. The variation in the average crystalline size and lattice parameter is related to RE ion doping. The Mössbauer spectra of CoRExFe2−xO4 are two sets of magnetic six-wire peaks that indicate the ferrimagnetic behavior of the sample. The calcination temperature greatly influences the absorption area of Mössbauer for CoFe2O4, indicating that the calcination temperature affects the iron ion content at the octahedral B and tetrahedral A sites. Additionally, scanning electron microscopy measurements of the substituted specimens reveal that the ferrite powders are nanoparticles. With an increase in RE ions, the coercivity increases, and the saturation magnetization changes obviously. The XRD characterization of Co0.7Zn0.3LaxFe2−xO4 shows that the main crystalline phase of the sample is the cubic spinel structure phase, and there are fewer secondary crystalline phases. The lattice parameter tends to decrease with the substitution of La3+ ions. The average grain size decreased significantly with the increase in La content. From ferrimagnetic state transition to relaxation behavior, the hyperfine magnetic field decreases in La concentration by room temperature Mössbauer spectra. With the substitution of La3+ ions, both the saturation magnetization and coercivity of the samples were reduced, and the coercivity of all samples was lower.
Funding Information
  • National Natural Science Foundation of China (12164006, 11364004)

This publication has 50 references indexed in Scilit: