Zinc oxide nanoparticles from microwave-assisted solvothermal process: Photocatalytic performance and use for wood protection against xylophagous fungus

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Nano- and micro-oxides are promising materials due to several interesting characteristics such as photocatalytic and antimicrobial role. In this work, zinc oxide nanorods were obtained by microwave-assisted solvothermal process and their photocatalytic performance and action for wood protection against wood-decay fungus was studied. The morphological (scanning electron microscopy and transmission electron microscopy analyses), microstructural (X-ray powder diffraction analysis) and chemical (infrared spectroscopy) characteristics of the oxide-based nanostructures were investigated. Moreover, photocatalytic performance was evaluated using methylene blue and methyl orange. The nanostructured zinc oxide was impregnated to pinewood samples at 1–5% content and tested for decay resistance using a white-rot fungus. Zinc oxide nanorods agglomerated as urchin-like structures presented high crystallinity, high purity, and high photocatalytic activity. Zinc oxide impregnation was effective in improving pinewood decay resistance, yielding similar protection compared to traditional wood preservative.

This publication has 25 references indexed in Scilit: