Preparation and Characterization of PHBV/PCL-Diol Blend Films

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Biodegradable thin films based on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and poly(caprolactone diol) (PCL-diol) blend were developed using the solution casting method. PHBV is biodegradable, biocompatible, and produced naturally by bacterial activity, but its use is restricted by high crystallinity and low resistance to thermal degradation with melting temperatures close to degradation thus narrowing the processing window. Solution casting was chosen as a cost-effective method reducing energy consumption and avoiding thermal degradation during processing. The increase in PCL-diol in blend composition (40–60 wt%) enhances the film-forming ability of PHBV and the wettability along with the decrease in the roughness of the resulting materials as revealed by contact angle measurements, scanning electron microscopy (SEM), and atomic force microscopy (AFM). Optimal composition in terms of filmogenity and surface structure has been achieved by the addition of PCL-diol in the amount of 60 wt%. FTIR confirmed the expected chemical structures with no evidence of chemical interactions between the two polymers.
Funding Information
  • Provincial Secretariat for Higher Education and Scientific Research, Autonomous Province of Vojvodina, Republic of Serbia (142-451-3949/2023, 142-451-3497/2023-01/01, 451-03-47/2023-01/200134, 451-03-47/2023-01/200156)
  • Ministry of Science, Technological Development and Innovation, Republic of Serbia (142-451-3949/2023, 142-451-3497/2023-01/01, 451-03-47/2023-01/200134, 451-03-47/2023-01/200156)

This publication has 24 references indexed in Scilit: