The effect of modifying the nanostructure of gelatin fiber scaffolds on early angiogenesis in vitro and in vivo

Authors:
Publisher website
Google Scholar
Abstract
Early angiogenesis is one of the key challenges in tissue regeneration. Crosslinking mode and fiber diameter are critical factors to affect the adhesion and proliferation of cells. However, whether and how these two factors affect early angiogenesis remain largely unknown. To address the issue, the optimal crosslinking mode and fiber diameter of gelatin fiber membrane for early angiogenesis in vivo and in vitro were explored in this work. Compared with the post crosslinked gelatin fiber membrane with the same fiber diameter, the 700 nm diameter in situ crosslinked gelatin fiber membrane was found to have smaller roughness (230.67 ± 19 nm) and stronger hydrophilicity (54.77° ± 1.2°), which were suitable for cell growth and adhesion. Moreover, the in situ crosslinked gelatin fiber membrane with a fiber diameter of 1000 nm had significant advantages in early angiogenesis over the two with fiber diameters of 500 and 700 nm by up-regulating the expression of Ang1, VEGF, and integrin- β 1. Our findings indicated that the in situ crosslinked gelatin fiber membrane with a diameter of 1000 nm might solve the problem of insufficient blood supply in the early stage of soft tissue regeneration and has broad clinical application prospects in promoting tissue regeneration.
Funding Information
  • Stomatological Hospital of Southern Medical University (No. PY2019001)
  • Foshan High-level Hospital Construction Project (DFJH202010 to Zhang Xueyang)

This publication has 35 references indexed in Scilit: