Investigating iodine-induced stress corrosion cracking of zirconium alloys using quantitative fractography
Authors:
- Conor GillenCGConor Gillen
- Alistair GarnerAGAlistair Garner
- Clara AnghelCAClara Anghel
- Philipp FrankelPFPhilipp Frankel
- 1 October 2020
- journal article
- research article
- Published by Elsevier in Journal of Nuclear Materials
- Vol. 539
Abstract
No abstract availableFunding Information
- EPSRC
- EP
- EPSRC
- EP
- EPSRC Programme (MIDAS [EP/S01702X/1])
This publication has 26 references indexed in Scilit:
- Iodine-Induced Stress Corrosion Cracking of Zircaloy-4: Identification of Critical Parameters Involved in Intergranular to Transgranular Crack PropagationSolid State Phenomena, 2011
- Proton irradiation effect on microstructure, strain localization and iodine-induced stress corrosion cracking in Zircaloy-4Journal of Nuclear Materials, 2009
- Strain-hardening influence on iodine induced stress corrosion cracking of Zircaloy-4Journal of Nuclear Materials, 2008
- Deformation–corrosion interactions for Zr alloys during I-SCC crack initiationJournal of Nuclear Materials, 1999
- Pellet-clad interaction (PCI) failures of zirconium alloy fuel cladding — A reviewJournal of Nuclear Materials, 1990
- Effects of material condition on the iodine SCC susceptibility of zircaloy-2 claddingJournal of Nuclear Materials, 1982
- Threshold conditions for iodine-induced stress corrosion cracking of unirradiated zircaloy-4 tubing under internal pressurizationJournal of Nuclear Materials, 1979
- Factors affecting stress corrosion cracking of zircaloy in iodine vapourJournal of Nuclear Materials, 1972
- Fracture of zirconium alloys in iodine vapourJournal of Nuclear Materials, 1971
- Control of hydride orientation in zircaloyJournal of Nuclear Materials, 1963