Polycrystal anelasticity at near‐solidus temperatures

Authors:
Publisher website
Google Scholar
Abstract
Elasticity, anelasticity, and viscosity of polycrystalline aggregates were measured at the near‐solidus temperatures ranging from below to above the solidus temperature (Tm). The result shows that the mechanical effects of the partial melting are twofold; changes just below the solidus temperature in the absence of melt and changes at the solidus temperature due to the onset of partial melting. As homologous temperature (T/Tm) increases from about 0.92 to 1, high‐frequency part of the attenuation spectrum significantly grows. Viscosity of the grain boundary diffusion creep is also reduced in this temperature range. These changes are caused by a solid‐state mechanism and have a large amplitude even for the samples which can generate very small amounts of melt at the solidus temperature. At the onset of melting, further increases in the elastic, anelastic, and viscous compliances occur. These changes are caused by the direct effects of the melt phase and are very small for the samples with very small melt fractions. Mechanical properties of a partially molten aggregate are determined by these twofold changes, and when melt fraction is small, the former changes are dominant. We performed a parameterization of the present experimental results and applied the obtained empirical formula to the seismic tomographic data in the upper mantle. The present model explains well the steep reduction of the seismic shear wave velocity in the oceanic lithosphere just below the solidus temperature.
Funding Information
  • Engineering and Physical Sciences Research Council (EP/K032208/1)

This publication has 39 references indexed in Scilit: