Lithium Niobate Crystal with Embedded Au Nanoparticles: A New Saturable Absorber for Efficient Mode‐Locking of Ultrafast Laser Pulses at 1 µm

Authors:
Publisher website
Google Scholar
Abstract
Plasmonic Au nanoparticles embedded in LiNbO3 crystals as efficient saturable absorbers to realize 74.1 ps mode‐locked laser pulse generation at 1 µm are reported. The system is fabricated by Au ion implantation and subsequent annealing, a well‐developed chip technology. The strong optical absorption band peaking at 640 nm is observed due to the localized surface plasmon resonance. Z‐scan investigation shows that the LiNbO3 crystals with embedded Au nanoparticles possess ultrafast saturable absorption properties at near‐infrared 1 µm wavelength. With this feature the Au nanoparticles embedded LiNbO3 wafer is applied as saturable absorber into a laser‐written Nd:YVO4 waveguide platform. Stable laser pulses at 1064 nm based on an efficient passive Q‐switched mode‐locking process, reaching a fundamental repetition rate of 6.4 GHz and a pulse duration of 74.1 ps, are obtained. Since LiNbO3 has broadband applications in various optical systems, this work opens the way to develop intriguing devices in LiNbO3‐based photonic circuits by using embedded metallic nanoparticles.
Funding Information
  • National Natural Science Foundation of China (11535008, 61522510)
  • Science and Technology Commission of Shanghai Municipality (17XD1403900)

This publication has 59 references indexed in Scilit: