Fiber cement boards modified with styrene-acrylic copolymer: An approach to address dimensional stability and cellulose fiber preservation

Authors:
Publisher website
Google Scholar
Abstract
The performance of polymers such as acrylics, styrene-acrylics, styrene-butadiene, ethylene vinyl acetate, type added in cementitious composites are well reported in the literature to boost properties in the fresh mortar stage as workability, anti-bleeding, and hard stage as deformation, adhesion strength, crack bridging, cohesion, durability and reduced water uptake. Polymer treatment was performed in fiber cement boards by adding 5% w/w (dry basis) of styrene-acrylic copolymer aiming to investigate the impact on the mechanical and physical properties at initial curing period (28 days) and after the 200 soak and drying ageing cycles. Dimensional stability at 28 days and the cellulose fiber/cement interface transition zone were assessed by scanning electron microscopy combined with dispersive energy X-ray spectroscopy (EDS). These experiments confirmed that the water absorption value in polymer modified cement boards was reduced by 50% after the ageing cycles when compared to the unmodified boards. Additionally, improvements on board’s rigidity with reduction of modulus of elasticity (MOE) values up to 40% and 15% reduction of board shrinkage was noticed, enhancing boards dimensional stability and preventing fibers from the mineralization process by keeping the cellulose fiber adhered on the cementitious matrix, providing a dense and cohesive fiber-cement interface transition zone after the ageing cycles. This achievement can open important fields of application for the reinforcement of flat panels.

This publication has 26 references indexed in Scilit: