Doping the Undopable: Hybrid Molecular Beam Epitaxy Growth, n-Type Doping, and Field-Effect Transistor Using CaSnO3

Authors:
Publisher website
Google Scholar
Abstract
The alkaline earth stannates are touted for their wide band gaps and the highest room-temperature electron mobilities among all of the perovskite oxides. CaSnO3 has the highest measured band gap in this family and is thus a particularly promising ultrawide band gap semiconductor. However, discouraging results from previous theoretical studies and failed doping attempts had described this material as "undopable". Here we redeem CaSnO3 using hybrid molecular beam epitaxy, which provides an adsorption-controlled growth for the phase-pure, epitaxial, and stoichiometric CaSnO3 films. By introducing lanthanum (La) as an n-type dopant, we demonstrate the robust and predictable doping of CaSnO3 with free electron concentrations, n3D, from 3.3 × 1019 cm-3 to 1.6 × 1020 cm-3. The films exhibit a maximum room-temperature mobility of 42 cm2 V-1 s-1 at n3D = 3.3 × 1019 cm-3. Despite having a comparable radius as the host ion, La expands the lattice parameter. Using density functional calculations, this effect is attributed to the energy gain by lowering the conduction band upon volume expansion. Finally, we exploit robust doping by fabricating CaSnO3-based field-effect transistors. The transistors show promise for CaSnO3's high-voltage capabilities by exhibiting low off-state leakage below 2 × 10-5 mA/mm at a drain-source voltage of 100 V and on-off ratios exceeding 106. This work serves as a starting point for future studies on the semiconducting properties of CaSnO3 and many devices that could benefit from CaSnO3's exceptionally wide band gap.
Funding Information
  • Division of Graduate Education (DGE-2139899)
  • Air Force Office of Scientific Research (FA9550-19-1-0245, FA9550-21-0460, FA9550-21-1-0025)
  • H2020 Marie Sklodowska-Curie Actions (101063432)
  • Solar Energy Technologies Office (DE-EE0009344)
  • Division of Materials Research (DMR-2011824, DMR-2235208, DMR-2306273)

This publication has 51 references indexed in Scilit: